A. Falahati:
"Warmstauchversuche zur Ermittlung der Fließspannungskurven von Cu und CuSn8 zwischen 0°C und 500°C";
2007; 11 pages.

Hot-compression tests were carried out on cylindrical and Ring-shaped
samples of Cu and CuSn8 alloys from room temperature to 500°C. The flow
stress of CuSn8 alloy compared to Cu from room temperature up to 500 ° C
showed significantly higher values.
There exists fluctuations during the compression tests in the true flow
stresses of CuSn8 materials from about 150 °C to 300 °C, which were
reproducible and could be referred to as CuSn8 material property. The
hardness of the samples after compressing with 0.8 true strain and air
cooling were measured and were compared with each other.

Es wurden Warmfestigkeitsuntersuchungen an zylindrischen Proben und
Dichtscheiben aus Cu /CuSn8 Legierungen durchgeführt. Die Fließspannungen
der CuSn8 Legierung zeigten im Vergleich zu den Fließspannungen bei Kupfer
bei Raumtemperatur bis 500 °C deutlich höhere Werte.
Bei CuSn8 Materialien gibt es von etwa 150°C bis 300°C während der Stauchung
Schwankungen in der wahren Druckspannung, welche reproduzierbar und auf
Eigenschaften des Materials zurückzuführen sind. Die Härte der gestauchten
Proben wurde nach 0,8 wahre Stauchung und Luftabkühlung gemessen und
miteinander verglichen.

Kupfer Legierung, CuSn8, Warmfestigkeit, Fließspannung, Bronze